Investigation of Reasons for Damage to a Steel Pipeline Used For the Injection of Formation Waters
Robert Jachym, Piotr Gotkowski, Jarosław Gazdowicz
The article presents results of test concerning reasons for the failure of
a steel pipeline (DN 80) used for the injection of formation waters. The tests revealed
that the perforation and subsequent material losses in the wall of the DN
80 pipeline made of steel L360NB were caused by deposit corrosion.
doi: 10.17729/ebis.2020.3/3